Pitch-based carbon fiber is a carbon fiber material made from petroleum asphalt or coal tar asphalt. It is characterized by abundant raw materials, low cost, high carbonization rate, and low product cost. High-performance pitch-based carbon fiber has outstanding tensile modulus and excellent conductivity, making it suitable for use as a […]

The production process for PAN-based carbon fibers is as follows: polymerization of the precursor solution—spinning—preoxidation—carbonization—graphitization—surface treatment. Specifically: Polypropylene monomers are polymerized to form the spinning solution, which is then spun into fibers. The finished raw fibers are reacted in a multi-stage oxidation furnace under an air atmosphere to produce pre-oxidized

Structural Characteristics of Polyacrylonitrile-Based Carbon Fibers   Polyacrylonitrile (PAN)-based carbon fibers are a type of inorganic fiber material with a carbon content of over 90%, appearing black in color. The diameter of the fibers varies depending on their specific performance requirements. PAN-based carbon fibers exhibit a hybrid structure comprising both

Throat Liner Ablation-resistant Carbon-carbon Composites Products   In the field of weaponry, the throat liner is a critical high-temperature component in various types of rocket projectiles. During its service life, it must withstand temperatures of approximately 3,000°C, internal gas pressures exceeding 15 MPa, and high-speed, high-temperature gas erosion. Traditional high-silica

Since its emergence in 1958, carbon-carbon composite materials have attracted widespread attention worldwide due to their outstanding performance. Many industrialized countries have invested significant human, material, and financial resources into the research and development of this material, continuously improving its performance and expanding its application scope. Over the past few